Complutense University Library

Estudio del comportamiento de dos tratamientos antigraffiti como protectores de materiales de construcción : interacción antigraffiti-substrato, propiedades y durabilidad

Carmona Quiroga, Paula María (2010) Estudio del comportamiento de dos tratamientos antigraffiti como protectores de materiales de construcción : interacción antigraffiti-substrato, propiedades y durabilidad. Tesis PhD.

[img]
Preview
PDF
13MB
View download statistics for this eprint

==>>> Export to other formats

Abstract

A los tradicionales agentes de
deterioro de los materiales de
construcción, agua, contaminantes
atmosféricos, agentes biológicos, etc.,
hay que unir las pintadas y la suciedad
con las que contribuye el hombre de
forma directa. En las ciudades, los
graffiti están sobre casi cualquier
superficie, pero es en los edificios,
especialmente en los históricos donde
provocan un mayor impacto y deterioro.
Para combatir este problema,
han sido desarrollados los productos
antigraffiti, que protegen las superficies
de los materiales de construcción,
impidiendo que la pintura penetre en sus
sistemas porosos, o se adhiera a las
superficies, facilitando de esta forma su
posterior limpieza (con agua a presión,
productos químicos, etc.).
La memoria contenida en este
volumen evalúa el comportamiento de
dos de estos productos antigraffiti, un
nuevo compuesto sintetizado en el
Instituto de Cerámica y Vidrio (CSIC),
Ormosil de Zr, y un producto comercial
de naturaleza fluorada (Protectosil
Antigraffiti® de Degussa), sobre la
superficie de cinco materiales de construcción; mortero de cemento, mortero
de cal, caliza, granito y ladrillo, en
términos de compatibilidad
(modificación de las propiedades
petrofísicas), interacción (profundidad
de penetración, formación de enlace
químico y modificación de centros
activos), eficacia (repelencia a las
pintadas y al agua) y durabilidad
(resistencia frente a ciclos hielodeshielo,
radiación UV o atmósfera
contaminada), dentro del proyecto
“Tratamientos superficiales en la
conservación de los materiales de
construcción: bases científicas y diseño
de nuevos productos polifuncionales”
(MAT 2003-08343).
Los resultados de cromatografía
de gases inversa señalan que de los dos
antigraffiti es el Protectosil (más
concentrado) el que actúa más
eficientemente en la reducción de la
energía superficial del mortero de cal, la
caliza y el granito. Este hecho explicaría
los mejores resultados en la limpieza de
los graffiti alcanzados en los materiales
impregnados con este producto,
claramente influenciados por la
porosidad, cohesión y
fundamentalmente rugosidad de los
substratos.
The damage caused by the
traditional agents of construction
material decay, namely water, air
pollutants, biological agents and so on,
is accentuated by direct human action
in the form of graffiti and soiling. While
graffiti can be found on nearly any
surface in cities, their effects – visual
impact and deterioration – are
especially pernicious in buildings,
historic buildings in particular.
Anti-graffiti coatings have been
developed to combat this problem by
protecting the surface of construction
materials to prevent paint from
penetrating their pore systems or from
adhering to the surface, thereby
facilitating subsequent cleaning
operations (with pressurized water,
chemical products and so on).
The present report evaluates the
behaviour of two such anti-graffiti
coatings, a new compound synthesized
at the Ceramics and Glass Institute (a
Spanish National Research Council,
CSIC, body), Zr Ormosil, and a
commercial fluorinated product
(Protectosil Antigraffiti®, manufactured
by Degussa). They were tested on five
construction material surfaces: cement mortar, lime mortar, limestone, granite
and brick. The parameters studied were
compatibility (modification of
petrophysical properties), interaction
(penetration depth, chemical bonding
and modification of active centers,
effectiveness (paint and water
repellence) and durability (resistance to
freeze-thaw cycles, UV radiation and
polluted air) under the project “Surface
treatments for the conservation of
construction materials: scientific
fundamentals and design of new multipurpose
products” (MAT 2003-08343).
The inverse gas chromatography
findings showed that of the two
coatings, Protectosil (more highly
concentrated) reduced the surface
energy in lime mortar, limestone and
granite more effectively. This would
explain the more thorough cleaning of
graffiti attained in the materials
impregnated with this product, a result
that was clearly related to the porosity,
cohesion and especially the roughness
of the substrates.

Item Type:Thesis (PhD)
Additional Information:Tesis de la Universidad Complutense de Madrid, Facultad de Ciencias Geológicas, Departamento de Petrología y Geoquímica, leída el 26-02-2010
Directors:
DirectorsDirector email
Blanco Varela, María TeresaUNSPECIFIED
Martínez Ramírez, SagrarioUNSPECIFIED
Uncontrolled Keywords:Materiales de construcción, Piedra, Graffiti
Subjects:Sciences > Geology > Petrology
Sciences > Geology > Geochemistry
ID Code:11305
Deposited On:05 Nov 2010 09:59
Last Modified:06 Feb 2014 09:01

Repository Staff Only: item control page