Growth and characterization of Fe1-xGax thin films from citrate-based electrolytes

Impacto

Descargas

Último año

Ranchal Sánchez, Rocío y Maestre Varea, David (2014) Growth and characterization of Fe1-xGax thin films from citrate-based electrolytes. Journal of Physics D: Applied Physics, 476 (35). ISSN 0022-3727

[img]
Vista previa
PDF
225kB

URL Oficial: http://dx.doi.org/10.1088/0022-3727/47/35/355004


URLTipo de URL
http://iopscience.iop.orgEditorial


Resumen

In this work we report on the growth of Fe_(1-x)Gax films by means of the electrodeposition technique in baths containing sodium citrate as an antioxidant agent. We have investigated the effect of the electrolyte composition in terms of its Ga content on the structural and magnetic properties. Our experimental results indicate that for the optimized bath composition, O-free Fe_(1-x)Gax alloys can be achieved for a potential of E = -1.4 V and magnetic stirring at 500 rpm. Both, the composition and the coercivity of the samples deposited from this electrolyte can be tuned by means of the duration of the rest pulse at E = -1.12 V. However, when the composition of the bath is not optimized the films exhibit a large amount of O that cannot be dissolved during the rest pulse. Our experimental results show that O-free Fe_(1-x)Ga_x alloys with a Ga content around 19 at. % and optimum magnetic properties can be


Tipo de documento:Artículo
Información Adicional:

©IOP Publishing Ltd.
This work has been financially supported through the projects MAT2011-28751-C02 and MAT 2012-31959 of the Spanish Ministry of Science and Innovation. We thank “CAI Difracción de rayos-X” of UCM for the x-ray diffractometry measurements.

Palabras clave:Fe-Ga; Magnetostrictive Fe_(1-X)Ga_x; Electrodeposition; Alloys
Materias:Ciencias > Física > Física de materiales
Ciencias > Física > Física del estado sólido
Código ID:33515
Depositado:09 Oct 2015 15:52
Última Modificación:13 Oct 2015 08:15

Descargas en el último año

Sólo personal del repositorio: página de control del artículo