A predictive formula of the contraction stress in restorative and luting materials attending to free and adhered surfaces, volume and deformation

Impacto



Miguel, A. de y Macorra García, José Carlos de la (2001) A predictive formula of the contraction stress in restorative and luting materials attending to free and adhered surfaces, volume and deformation. Dental Materials, 7 . pp. 241-246.

[img]
Vista previa
PDF
128kB


Resumen

Objectives: To find a predictive formula of stress, considering the surfaces (free, adhered) involved, the volume and characteristics of material and the deformation of the measuring system.
Materials and methods: 231 samples of five chemically cured restoratives (Silar (SIL, 23), Clearfil F2 (CLE, 39), P10 (P10, 33), Concise (CON, 30), Isopast (ISO, 28)) and four luting (3M Experimental 241 (EXM, 20), Variolink II (VAR, 13), Vitremer LC (VTM, 20) and Dyract Cem (DYR, 25)) materials were allowed to polymerize until they reached a maximum tension (Tmax, 25 min) between six pairs (B 5.81, 8.5,
11.26, 12.42, 17.02, 23.14 mm) of polished metallic discs (range of distances: 0.02±5.9 mm) mounted in a tension machine. The deformation of the measuring system was measured for the recorded forces.
Results: A descriptive non-linear formula was found that individualizes the material's characteristics
(K) that considers volume (Vol), free (FS) and adhered (AS) surfaces and deformation (Def) of the system for each force. This formula renders good correlation (material K (r2 coeffcient)): SIL 0.9998 (0.995), CLE 1.0062 (0.989), P10 1.0224 (0.990), CON 0.9908 (0.992), ISO 0.9648 (0.974), EXM 1.0083 (0.991), VAR 0.9777 (0.996), VTM 0.9925 (0.993), DYR 0.9971 (0.997) between actual Tmax and calculated Tension. There are statistically signifcant differences between K values of both (restorative and luting) groups. Signifcance: Predictive parameters have influence in a different way to what is actually considered, if the system is allowed to have
deformation, as occurs naturally and volume and material's characteristics are considered.


Tipo de documento:Artículo
Palabras clave:Polimerization, Stress, Contraction, Composite resin, Configuration
Materias:Ciencias Biomédicas > Odontología > Materiales dentales
Código ID:4929
Depositado:04 Jul 2005
Última Modificación:06 Feb 2014 07:42

Sólo personal del repositorio: página de control del artículo