The influence of SiNx:H film properties on the electrical characteristics of metal-insulator-semiconductor devices

Impacto

Downloads

Downloads per month over past year

Mártil de la Plaza, Ignacio and González Díaz, Germán and García, S. and Fernández, M. (1997) The influence of SiNx:H film properties on the electrical characteristics of metal-insulator-semiconductor devices. Semiconductor Science and Technology, 12 (12). pp. 1650-1653. ISSN 0268-1242

[img] PDF
Restringido a Repository staff only hasta 31 December 2020.

105kB

Official URL: http://dx.doi.org/10.1088/0268-1242/12/12/018


URLURL Type
http://iopscience.iop.org/Publisher


Abstract

SiNx:H thin films were deposited by the electron cyclotron resonance plasma method at low substrate temperature (200 degrees C) to fabricate metal-insulator-semiconductor devices. The effects of film properties on the electrical characteristics of two different devices, SiNx:H/Si and SiNx:H/InP, were analysed according to the C-V high-low frequency method. The results show that, in the devices based on Si, the presence of N-H bonds in the SiNx:H film increases the density of trapping centres at the insulator/semiconductor interface. This behaviour was analysed by the model recently proposed by Ying (1995 J. Vac. Sci. Technol. B 13 1613) for nitrided SiO2/Si interfaces. For the SiNx:H/InP capacitors, the electrical characteristics of the interface were strongly dependent on the SiNx:H composition. When the nitrogen to silicon ratio of the film was N/Si = 1.49, the minimum of the interface trap density was 2 x 10(12) cm(-2) eV(-1) This value was similar to the same data reported by other authors on devices where the InP surface was sulphur passivated. This suggests that nitrogen atoms of the insulator play some passivation role at the InP surface. The plasma exposure of the semiconductor surface during the deposition of the SiNx:H film promotes the formation of phosphorus vacancies at the InP surface. Nitrogen atoms may fill these vacancies and this gives rise to an insulator/semiconductor interface with few defects.


Item Type:Article
Additional Information:

© IOP Publishing Ltd. The authors would like to thank E. Iborra for the facilities for the infrared characterization of films. This research was partially supported by the Spanish CYCIT under grant No TIC 93/0175.

Uncontrolled Keywords:Chemical-Vapor-Deposition, Silicon-Nitride, Plasma, Temperasture, Remote, Passivation, Interfaces.
Subjects:Sciences > Physics > Electricity
Sciences > Physics > Electronics
ID Code:27067
Deposited On:13 Oct 2014 15:08
Last Modified:10 Dec 2018 14:58

Origin of downloads

Repository Staff Only: item control page