Analysis of sealing vs tensile bond strength of eight adheisve restorative material systems



Último año

Del-Nero Beneitez, María Olga y Escribano, Nuria Isabel y Macorra García, José Carlos de la (2000) Analysis of sealing vs tensile bond strength of eight adheisve restorative material systems. Journal of Adhesive Dentistry, 2 . pp. 117-127.

Vista previa


Purpose: Using a simulated perfusion system, the intent was to determine: 1) the sealing ability of eight
restorative materials (five composite resins and three compomers) used together with their corresponding dentin bonding systems, 2) their tensile bond strength, and 3) the correlation (if any) between both parameters.
Materials and Methods: Permeability in crown segments from sound human third molars (n = 140) subjected to simulated perfusion (32 cm of distilled water) was measured before and after restoring with each material, and the percentage of decrease in permeability ((PPD) was recorded. Specimens were tater subjected to tensile tests to determine the tensile bond strength (TBS) of the interface. Finally, parameters were analyzed for correlation.
Results: For the eight adhesive systems, the percentage of reduction in permeability was relatively hlgh [mean in %, (SD)]: F2000 93.6 (5.7),S B188.6 (11.31,S SC 86.0 (5.7), PB20 81.1 (15.9)C,O M 77.5 (10.8), OPTS 75.3 (20.6)D,Y R 73.7 (12.7)S,S PR 65.5 (19.8)T.B S values were relatively low [mean (SD)], in MPa: F2000 1.8 (0.71, SB1 4.9 (1.4)S,S C 2.6 (1.4), PB20 4.3 (1.21,C OM 2.4 {1.1),O PTS 4.5 (1.7)D,Y R L6 (0.6), SSPR.4.2 (1.5). We could not demonstrate any statistically significant correlation between both parameters for these results (maximum significance [F20001: r = 0.39, p = 0.206).
Conclusion: No material completely ceased to filtrate through the interface. The low TBS values were probably due to the large size of adhesive areas. No significant correlation was found between PPD and TBS
for the materials tested. There was a statistically significant relationship (r2 = 0.063, p = 0.018) between
TBS and TEA (total bonded area), described by the equation TBS = 5.9 - 0.03'TBA.

Tipo de documento:Artículo
Palabras clave:dentin, sealing, perfusion
Materias:Ciencias Biomédicas > Odontología > Materiales dentales