Magnetic phase diagram of nanostructured zinc ferrite as a function of inversion degree delta



Downloads per month over past year

Cobos Fernández, Miguel Ángel and Presa Muñoz del Toro, Patricia de la and Llorente, I. and Alonso Rodríguez, José María and Garcia Escorial, A. and Marín Palacios, María Pilar and Hernando Grande, Antonio and Jiménez, J. A. (2019) Magnetic phase diagram of nanostructured zinc ferrite as a function of inversion degree delta. Journal of physical chemistry C, 123 (28). pp. 17472-17482. ISSN 1932-7447

[thumbnail of DeLaPresaP 23 Postprint+EMB 18-jul-2020.pdf]

Official URL:


Magnetic properties of spinel zinc ferrites are strongly linked to the synthesis method and the processing route since they control the microstructure of the resulting material. In this work, ZnFe_2O_4 nanoparticles were synthesized by the mechanochemical reaction of stoichiometric ZnO and alpha-Fe2O3, and single-phase ZnFe_2O_4 was obtained after 150 h of milling. The as-milled samples, with a high inversion degree, were subjected to different thermal annealings up to 600 ºC to control the inversion degree and, consequently, the magnetic properties. The as-milled samples, with a crystallite size of 11 nm and inversion degree delta = 0.57, showed ferrimagnetic behavior even above room temperature, as shown by Rietveld refinements of the X-ray diffraction pattern and superconducting quantum interference device magnetometry. The successive thermal treatments at 300, 400, 500, and 600 degrees C decrease delta from 0.15 to 0.18, affecting the magnetic properties. A magnetic phase diagram as a function of delta can be inferred from the results: for delta < 0.25, antiferromagnetism, ferrimagnetism, and spin frustration were observed to coexist; for 0.25 < delta < 0.5, the ferrimagnetic clusters coalesced and spin glass behavior vanished, with only a pure ferrimagnetic phase with a maximum magnetization of M_s = 3.5 mu_B remaining. Finally, for delta > 0.5, a new antiferromagnetic order appeared due to the overpopulation of nonmagnetic Zn on octahedral sites that leads to equally distributed magnetic cations in octahedral and tetrahedral sites.

Item Type:Article
Additional Information:

©2019 American Chemical Society
This work was supported by grants from the Spanish Ministry of Science and Innovation MAT2015-67557 -C2 -1-P

Uncontrolled Keywords:Cation distribution; ZnFe2O4 Nanoparticles; Temperature; Mossbauer; Behavior; Size; Degradation; Parameters; Memory; Oxide
Subjects:Sciences > Physics > Materials
Sciences > Physics > Solid state physics
ID Code:57231
Deposited On:17 Oct 2019 18:24
Last Modified:18 Jul 2020 23:01

Origin of downloads

Repository Staff Only: item control page